化合物简介
Ethylenebis(tetrabromophthalimide) is an additive fire retardant that is added to a polymer mixture to produce a blend. Ethylenebis(tetrabromophthalimide) is used in high impact polystyrene (HIPS), polyethylene, polypropylene, thermoplastic polyesters, polyamide, ethylene propylene-diene terpolymers (EPDM rubbers) and other synthetic rubbers, polycarbonate, ethylene copolymers, ionomer resins, epoxies, and textile treatments.
基本信息
中文名称
乙撑双四溴邻苯二甲酰亚胺
英文名称
4,5,6,7-tetrabromo-2-[2-(4,5,6,7-tetrabromo-1,3-dioxoisoindol-2-yl)ethyl]isoindole-1,3-dione
中文别名
1,2-双(四溴邻苯二甲酰亚胺)乙烷、乙撑双(四溴邻苯二甲酰胺)、阻燃剂 BT-93W
英文别名
Saytex BT 93、BT 93W、Saytex BT 93W、Citex BT 93、BT 93、BT-93D
CAS号
32588-76-4
分子式
C18H4Br8N2O4
分子量
951.467
精确质量
943.364
PSA
74.76
LOGP
7.5546
编号系统
UNII
B14GGF3PP8
物化性质
外观与性状
黄色粉末
密度
2.67
沸点
827.9ºC at 760 mmHg
熔点
446°C
闪点
454.5ºC
折射率
1.766
储存条件
Keep in a cool, dry, dark location in a tightly sealed container or cylinder. Keep away from incompatible materials, ignition sources and untrained individuals. Secure and label area. Protect containers/cylinders from physical damage.
安全信息
WGK Germany
3
海关编码
2925190090
生产方法及用途
生产方法
1.以四溴苯酐、甲醇、乙二胺为原料,经两步合成制得。先将四溴苯酐在甲醇中进行加热回流反应。得四溴邻苯二甲酸单甲酯。然后,加乙二胺甲醇溶液,继续进行回流反应,反应完后,冷却,过滤,干燥,得白色结晶状乙撑二铵双(四溴邻苯二甲酸单甲酯),再在直空及136℃下加热较长时间,即得乙撑双(四溴邻苯二甲酰胺)。
2.将四溴苯酐和甲醇加入反应釜,搅拌下加热至回流进行反应,反应2h后生成四溴邻苯二甲酸单甲酯:
3.加入乙二胺的甲醇溶液,继续在搅拌下进行加热回流反应。反应完成后,冷却、过滤、干燥,得白色结晶状亚乙基二胺双(四溴邻苯二甲酸单甲酯):
4.将亚乙二胺双(四溴邻苯二甲酸单甲酯)加入真空干燥箱,在真空下于136℃进行保温及脱除甲醇和水。将此白色晶体在真空加热条件下处理脱除甲醇和水,最后得黄色粉末状固体,即为产品EBT:
2.将四溴苯酐和甲醇加入反应釜,搅拌下加热至回流进行反应,反应2h后生成四溴邻苯二甲酸单甲酯:
3.加入乙二胺的甲醇溶液,继续在搅拌下进行加热回流反应。反应完成后,冷却、过滤、干燥,得白色结晶状亚乙基二胺双(四溴邻苯二甲酸单甲酯):
4.将亚乙二胺双(四溴邻苯二甲酸单甲酯)加入真空干燥箱,在真空下于136℃进行保温及脱除甲醇和水。将此白色晶体在真空加热条件下处理脱除甲醇和水,最后得黄色粉末状固体,即为产品EBT:
用途
1.本品是国外近期开发的添加型阻燃剂,具有优异的热稳定性能、抗紫外线性能、不挥发、不析出、无臭,特别是不影响制品的电性能,因此可用于电线、电缆、计算机部件及自动仪表原件中。本品可用于高抗冲聚苯乙烯、聚丙烯、聚乙烯、热塑性聚酯、尼龙、ABS树脂、乙丙共聚物以及聚碳酸酯等高分子材料。尤对环氧树脂胶黏剂的阻燃效果优异。亦可用于电线、电缆、计算机部件及自动仪表原件中。