化合物简介
Vanadium(IV) dioxide is an inorganic compound with the formula VO2. It is a dark blue solid. Vanadium(IV) dioxide is amphoteric, dissolving in non-oxidising acids to give the blue vanadyl ion, [VO]2+ and in alkali to give the brown [V4O9]2− ion, or at high pH [VO4]4−. VO2 has a phase transition very close to room temperature(~66°C). Electrical resistivity, opacity, etc, can change up several orders. Due to these properties, it has been widely used in surface coating, sensors, and imaging. Potential applications include use in memory devices.
基本信息
中文名称
氧化钒(IV)
英文名称
vanadium dioxide
中文别名
四氧化二钒、二氧化钒
英文别名
9,10-Didecyloxyanthracene、bis oxovanadium、bis n-decyloxy-9,10 anthracene、VANADIUM(IV) OXIDE
CAS号
12036-21-4
分子式
O2V
分子量
82.9403
精确质量
82.9338
PSA
34.14
LOGP
-0.2376
编号系统
MDL号
MFCD00049702
EINECS号
234-841-1
PubChem号
24852918
物化性质
密度
4.339 g/mL at 25ºC(lit.)
熔点
1967ºC
安全信息
安全说明
26-37/39
危险类别码
R36/38
危险品运输编码
UN3285
危险类别
6.1
包装等级
II
危险品标志
Xi
危险性描述
H315; H319
信号词
Warning
危险性防范说明
P305 + P351 + P338
危险标志
GHS07
生产方法及用途
生产方法
由五氧化二钒和三氧化二钒的固相反应合成。将化学计量的反应混合物装入石英管,抽真空密封,加热40～60h。最初在600℃下加热,接着加热到750～800℃,直至反应完。 只要严格控制固气相体系的氧化还原反应条件,也能制得组成比较一致的二氧化钒。例如:
(1)应用CO2H2混合缓冲气体 :将CO2和H2在常温下的分压比(PCO2/P
H2)从1000∶1调整到3000∶1,在1000～1400℃温度下的氧气分压调节为10-5～10-3atm(1atm=101 325kPa)。在这种气氛中,以五氧化二钒或三氧化二钒为起始原料,保持约20h以上,可以得到二氧化钒。
(2)应用干燥SO2气体 :在以五氧化二磷干燥的SO2气流中,于500～650℃,20～40h内,使五氧化二钒还原,或使三氧化二钒氧化,均可得到二氧化钒。
(1)应用CO2H2混合缓冲气体 :将CO2和H2在常温下的分压比(PCO2/P
H2)从1000∶1调整到3000∶1,在1000～1400℃温度下的氧气分压调节为10-5～10-3atm(1atm=101 325kPa)。在这种气氛中,以五氧化二钒或三氧化二钒为起始原料,保持约20h以上,可以得到二氧化钒。
(2)应用干燥SO2气体 :在以五氧化二磷干燥的SO2气流中,于500～650℃,20～40h内,使五氧化二钒还原,或使三氧化二钒氧化,均可得到二氧化钒。